HIGH PERFORMANCE STRUCTURAL ACRYLIC ADHESIVE in 25ml syringe
- Versatile structural adhesive that bonds a wide variety of substrates
- Bonding metal fasteners to molded composite parts
- Bonding aluminium and stainless steel lettering in sign manufacture
- Bonding automotive carbon fibre body panels
- Bonding GRP in the marine industry
- Bonding dissimilar metals for trailer fabrication
- Additional information
- Health & Safety Information
- HANDLING & APPLICATIONS
- Reviews (0)
a two component adhesive, designed for the quick, high strength bonding of a wide variety of materials such as plastics, metals and composites. Alpha 6010 adhesive system achieves the ultimate balance of mechanical strength and impact resistance whilst still remaining both quick and simple to use.
☛ Fast cure adhesive with fast strength build up
☛ Excellent bonding to a wide range of metals and plastics
☛ Easy to use
☛ High shear strength
☛ High impact strength
☛ Good chemical resistance
☛ No need for surface primers or conditioners
The following technical information and data should be considered representative or typical only. Therefore, the information should not be used for specification purposes.
✒ Mix Ratio 1:1 Part A to Part B
✒ Open Time (20°C) 5-7 minutes
✒ Cure Time (20°C) Cure Time: 9-12 minutes Full Cure: 24 hours
✒ Heat Resistance ‐55°C to 120°C
✒ Coverage (0.2mm bond line) 0.1 – 0.15 square metres per 25ml
25ml, 50ml, 400ml
Health & Safety Information
Alpha 6010 is classified as hazardous according to Directive EC 1272/2008. Please refer to the Alpha 6010 Safety Data Sheet for further health & safety information.
HANDLING & APPLICATIONS
The general application information presented here is based upon typical conditions determined by Alpha Adhesives & Sealants Limited testing. Our recommendations on the use of this product are based on methods believed to be reliable. It is advised that users conduct their own tests to determine the suitability of the product for their specific application.
Process Step Guidelines Surface Preparation All substrate surfaces should be abraded using abrasion paper or air-driven narrow belt sander. It is imperative that the surfaces are then cleaned of any dust, grit, loose material, wax, grease and oil using a suitable cleaner such as Alpha T559. Adhesive Application 1. Remove the cap from the twin syringe and attach the supplied mixer nozzle. Dispense a sufficient amount of adhesive to ensure both components are mixing equally.
- Apply the mixed adhesive on to one of the substrates.
- Assemble the substrates together carefully within the working life (5 to 7 minutes). Use clamps to hold together if necessary.
Remove any excess adhesive prior to curing using a suitable cleaner. It is much easier to remove excess whilst it is uncured. Curing Handling strength is achieved approximately 30 minutes after bonding. Full cure is achieved 24 hours after bonding. Cleaning A suitable solvent cleaner such as Alpha T559 should be used to clean uncured adhesive prior to curing. When fully cured, Alpha 6010 will require mechanical sanding to remove material.
Alpha 6010 should be stored in its original container, with the syringe cap tightly secured, in dry conditions and at temperatures between 5°C and 25°C. Alpha 6010 will keep satisfactorily for up to 12 months from date of manufacture if stored according to the recommended conditions.